^{3M BHT-HF Tape Polyester Film Acrylic Pressure-Sensitive Adhesive}

^{3M BHT-HF 聚酯薄膜膠帶 丙烯酸膠黏劑 鋰電池膠帶}

3M BHT-HF tape is mainly for the lithium ion secondary batteries manufacture with holding and insulation application. The tape is the polyester film uniformly coated with yellow acrylic pressure sensitive adhesive (PSA), which is specifically designed with excellent solvent resistance to fulfill under the electrolytic solution’s environment. It could be operated not only by manual but also by auto-taping machine. It meets halogen free requirement.

Total Thickness: 0.040mm

Breaking strength: 35  N/cm

Dielectrical Breakdown: 4 KV

Adhesion (180 deg peel): 2 N/cm

3M BHT-HF膠帶是鋰電池專用絕緣固定膠帶, 主要為與鋰電池加工製造廠設計 用於固定絕緣和绝緣保護鋰離子電池  耐130度C

材料: 符合無鹵 RoHS  聚酯薄膜polyester film 黃色丙烯酸膠黏劑  優秀耐溶劑 抗電解液性能及絕緣效果.

^{3M Electrical Tape 5 Clear Polyester Film Tape with Oil-Compatible, Acrylic Adhesive}

^{3M 聚酯薄膜膠帶 5 丙烯酸膠黏劑}

3M 5 Electrical Tape is a 1-mil, clear polyester film with a pressure-sensitive acrylic adhesive. A single-coated tape,
it features an adhesive system that offers resistance to most common cleaning solvents. for insulating applications requiring a thin, durable tape with high dielectric strength, such as for use in coil and capacitor and holding applications.
• Oil Resistant
• Resists most common cleaning solvents
• Transparent
• UL Recognized to 130°C

Adhesive: Acrylic
Backing: Polyester Film
Backing Thickness: 1.0 mil (0.025 mm)
Total Thickness: 2.5 mils (0.063 mm)
Color: Translucent
Temperature Class: 130°C (266°F)
Breaking Strength: 25 lbs./in (44 N/10 mm)
Elongation: 100%
Adhesion to Steel: 35 oz./in (3.8 N/10 mm)
Dielectric Strength: 5500V
Insulation Resistance: >1000000 megohms
Electrolytic Corrosion Factor: 1.0

厚 1mil 微透明聚酯薄膜,抗油,抗溶劑﹔適用於固定線圈及電容器。66M長

^{Tape 54 Polyester Film Tape With Thermosetting Rubber Adhesive}

^{聚酯薄膜膠帶 54 熱固橡膠粘劑}

3M Polyester Film Electrical Tape 54 is a 1 mil polyester film tape with a translucent rubber thermosetting adhesive.

3M Polyester Film Electrical Tape 54 is for use in fine wire coils where magnet wire serves to color code. Rated for use up to 130°C (266°F), it withstands higher temperature conditions than tapes with acetate film backing. 3M 54 Tape is especially suited for use is wrapping fine wire coils where magnet wire serves to color code.

Adhesive: Thermosetting Rubber
Backing: Polyester Film
Backing Thickness: 1.0 Mil
Total Thickness: 2.5 mils/.063mm
Color: Transparent
Temperature Class: 130°C /266°F
Dielectric Breakdown: 5,500 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 25 lbs./in. (44 n/10mm)
Elongation: (% at break) 100
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 45 oz./in. (4,9 n/10mm)

厚 1mil 薄膜，適用於極細漆包線圈而該漆包線能做標記用途。 微透明

^{Tape 56 Polyester Film With Thermosetting Rubber Adhesive}

^{聚酯薄膜膠帶 56 熱固橡膠粘劑}

3M Polyester Film Electrical Tape 56 is a 1 mil polyester film tape with a yellow rubber thermosetting adhesive. Designed for insulating applications requiring high dielectric strength with a thin, durable film backing. It has a rubber thermosetting adhesive coating and a low adhesion backsize coating which makes it suitable for automatic taping. It is used in applications of coil outerwrap, inner-layer insulation, capacitor wrap, and assorted other holding applications. The thermosetting rubber adhesive is aggressive and suited for adhering to oily magnet wire. By heat curing, the thermosetting adhesive can be made to resist common industry varnish solvents. UL Recognized for continuous use to 130°C (266°F).

Adhesive: Thermosetting Rubber
Backing: Polyester Film
Backing Thickness: 1.0 Mil
Total Thickness: 2.3 mils/.058mm    Length:  60M
Color: Yellow
Temperature Class: 130°C /266°F
Dielectric Breakdown: 5,500 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 25 lbs./in. (44 n/10mm)
Elongation: (% at break) 100
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 50 oz./in. (5,5 n/10mm)

厚 1mil 薄膜，黃色, 適用於130℃時的層間絕緣和線圈封包    長  60M

3M公司之#56電氣絕緣膠帶係使用熱固性橡膠，經過熱固程序 ( 120°C ; 3 hrs或 135°C ; 1.5 hrs 或 150°C ; 1 hrs )擇一處理後，其耐溶劑性會提昇至三級以上，(一般時其耐溶劑性為二級)。

^{Polyester Film Electrical Tape 57 With Thermosetting Rubber Adhesive}

^{聚酯薄膜膠帶 57 熱固橡膠粘劑}

3M Polyester Film Electrical Tape 57 is a 2 mil polyester film tape with rubber thermosetting adhesive. 3M Polyester Film Electrical Tape 57 is specified for insulating applications requiring a thin, durable tape with high dielectric strength, such as for wrapping coils and capacitors and holding applications. Rated for use up to 130°C (266°F), it withstands higher temperature conditions than tapes with acetate film backing.

Adhesive: Rubber Thermosetting
Backing: Polyester Film
Backing Thickness: 2.0 Mil
Total Thickness: 3.3 mils/.083mm
Color: Yellow
Temperature Class: 130°C /266°F
Dielectric Breakdown: 7000 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 50 lbs./in. (88 n/10mm)
Elongation: (% at break) 110
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 60 oz./in. (6,5 n/10mm)

厚 2mil 薄膜，用於需要較高電氣強度的線圈封包、層間絕緣及電容器封包。黃色

^{Polyester Film Electrical Tape 58 With Thermosetting Rubber Adhesive}

^{聚酯薄膜膠帶 58 熱固橡膠粘劑}

3M Polyester Film Electrical Tape 58 is a 2 mil polyester film tape with a translucent rubber thermosetting adhesive. 3M Polyester Film Electrical Tape 58 is for use in fine wire coils where magnet wire serves to color code. Use as a coil cover; layer insulation and capacitor wrap where higher electrical strength is desirable. Rated for use up to 130°C (266°F), it withstands high temperature conditions.

Adhesive: Rubber Thermosetting
Backing: Polyester Film
Backing Thickness: 2.0 Mil
Total Thickness: 3.3 mils/.083mm
Color: Transparent
Temperature Class: 130°C /266°F
Dielectric Breakdown: 7000 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 50 lbs./in. (88 n/10mm)
Elongation: (% at break) 110
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 60 oz./in. (6,5 n/10mm)

厚 2mil 薄膜，用於需要較高電氣強度的線圈封包、層間絕緣及電容器封包。微透明

^{Polyester Film Electrical Tape 74 With Thermosetting Rubber Adhesive}

^{聚酯薄膜膠帶 74 熱固橡膠粘劑}

3M Polyester Film Electrical Tape 74 is a 0.5 mil polyester film tape with a yellow rubber thermosetting adhesive, that provides good electrical strength for coil applications where space is at a premium. Rated for use up to 130°C (266°F).

Adhesive: Rubber Thermosetting
Backing: Polyester Film
Backing Thickness: 0.5 Mil
Total Thickness: 0.8 mils/0,02mm
Color: Yellow
Temperature Class: 130°C /266°F
Dielectric Breakdown: 3500 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 12 lbs./in. (21 n/10mm)
Elongation: (% at break) 100
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 20 oz./in. (2,2 n/10mm)

超薄層間絕緣膠帶 厚 0.5mil 薄膜，從形性好，在空間有限的線圈作封包，電氣性能佳。黃色

^{Double-Coated Polyester Film Tape 75 With Thermosetting Rubber Adhesive}

^{聚酯雙面薄膜膠帶 75 熱固橡膠粘劑}

3M Double-Coated Polyester Film Tape 75 is for use in bonding applications requiring a positive insulation barrier.
3M Double-Coated Polyester Film Tape 75 is specified for insulating applications requiring a double-coated thin, durable tape with high dielectric strength, such as for wrapping coils and capacitors and holding applications. Rated for use up to 130°C (266°F), it withstands higher temperature conditions than tapes with acetate film backing. 3M 75 Tape is especially suited for use in bonding applications requiring a positive insulation barrier.

Adhesive: Rubber Thermosetting
Backing: Polyester Film
Backing Thickness: 1.0 Mil
Total Thickness: 3.8 mils/0.096mm
Color: Yellow
Temperature Class: 130°C /266°F
Dielectric Breakdown: 6500 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 25 lbs./in. (44 n/10mm)
Elongation: (% at break) 100
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 45 oz./in. (4,9 n/10mm)

厚 1mil 薄膜，雙面，適用於需要絕緣作用的接合情況。黃色

^{3M 1298 Polyester Film, Flame-Retardant with Pressure Sensitive Acrylic Adhesive}

^{聚酯雙面薄膜膠帶 1298}

3M Electrical Tape 1298 is compatible with most commonly used magnet wire enamels, such as
polyurethane, formvar and polyester. Purchasers should conduct their own tests to determine the
compatibility of this tape with the insulation systems they use.

Flagging resistant /  Printable /  Solvent resistant without thermosetting / Flame retardant per UL Subject 510

Thickness: 2.5 mils (.063 mm)
Breaking Strength: 25 lb./in (44 N/10 mm)
Elongation: 100%
Adhesion to Steel: 40 oz/in (4.4 N/10 mm)
Dielectric Strength: 5500V
Temperature Class: 130°C
Insulation Resistance: >1000000 megohms
Electrolytic Corrosion Factor: 1.0
Copper Corrosion: None
Flammability: Passes

^{Polyester Film Electrical Tape 1318 Acrylic Adhesive Non-Halogenated}

^{聚酯薄膜膠帶 1318 丙烯酸膠黏劑 無鹵}

Available in yellow, white or black, the 3M Polyester Film Electrical Tape 1318-1 is a 1 mil polyester film tape with acrylic adhesive, and has excellent flagging and solvent resistance. Printable.

3M Polyester Film Electrical Tape 1318-1 is specified for insulating applications requiring a thin, durable tape with high dielectric strength, such as for wrapping coils and capacitors and holding applications. This tape has an excellent flagging resistance and solvent resistance, making it well suited for applications where cleaning solvents and mineral oil are present. It consists of materials that are represented in many UL Recognized Insulation Systems and has a UL 130°C temperature rating. It offers good wet grab, excellent shelf life, smooth, even unwind and is suitable for printing and use on automated equipment.. 3M 1318 Tape is especially suited for applications such as wrapping coils, capacitors, wire harnesses, transformers, shaded pole motors and fractional horsepower motors.

Adhesive: Acrylic
Backing: Polyester Film
Backing Thickness: 1.0 Mil
Total Thickness: 2.5 mils/0.063mm
Color: Yellow, White, Black
Temperature Class: 130°C /266°F
Dielectric Breakdown: 5500 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 25 lbs./in. (44 n/10mm)
Elongation: (% at break) 100
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 30 oz./in. (3,3n/10mm)

1318-1 PET Film Tape厚 1mil 薄膜，抗鬆脫、抗溶劑﹔用於變壓器線圈的外層封包,線圈和電容器的外層封包，可在表面印刷.   白, 透明    為無鹵  66M長  黃, 黑,

Tape 1318-2

Adhesive: Acrylic
Backing: Polyester Film
Backing Thickness: 1.0 Mil
Total Thickness: 3.3 mils/0.088mm
Color: Yellow, White, Black
Temperature Class: 130°C /266°F
Dielectric Breakdown: 7000 Volts
Insulation Resistance: (megohms) >1000000
Breaking Strength: 50 lbs./in. (88 n/10mm)
Elongation: (% at break) 100
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 30 oz./in. (3,3n/10mm)

1318-2 Tape 厚 2mil 薄膜

^{3M Polyester Film Electrical Tape 1683 Acrylic Adhesive Polyester Film Tape with Electrical Insulation Grade Acrylic
Pressure-Sensitive Adhesive 絕緣遮光膠帶}

^{3M 聚酯薄膜膠帶 1683 丙烯酸膠黏劑   絕緣遮光膠帶}

3M™ 1683 tape is an electrical insulating polyester film tape and meets non-halogen requirement. It offers
good light shielding, proper adhesion level to be suitable for use on automated equipment.
Bromide content<900ppm; Total halogen content<1500ppm
Solvent resistant without thermosetting
Electrical insulating
Non-corrosive
Good light shielding
Excellent shelf life

Adhesive: Black color electrical grade acrylic
Backing: 0.5 mil polyester film
Total Thickness: 1.2 mils / 0.030 mm
Dielectric Breakdown:  3500 Volts
Insulation Resistance @ 23 C & 96% RH, 96 hrs >1.0 x 10 E+12 ohms
Breaking Strength 4.5 (kg/in)
Elongation (% at break) 50
Adhesion to Steel 0.85/ (kg/in)

• 為無鹵素黑色絕緣膠帶
• 抗翹邊和抗溶劑
• 良好的絕緣性能
• 提供良好之遮光、修飾效果

^{Flame-Retardant Tape 1350 with Polyester Film and Acrylic Pressure-Sensitive Adhesive}

^{聚酯薄膜膠帶 1350 1350F-1 1350F-2 1350T-1 1350T-3 丙烯酸膠黏劑  PET Tape  RoHS}

^{紅色/綠色電氣絕緣膠帶停產}

3M 1350 Tape is an electrical insulating polyester film tape, which meets the flame-retardancy requirements of UL 510. It consists of materials that are represented in many UL Recognized Insulation Systems and has a UL 130°C temperature rating. It also offers excellent flagging and solvent resistance; good wet grab; smooth, even unwind and is suitable for use on automated equipment. For applications such as wrapping coils, capacitors, wire harnesses, transformers, shaded pole motors and fractional horsepower motors. 2 diffferent size: 1 mil film & 2 mil film backing

Properties: 1 mil Film (1350F-1) / 2 mil Film (1350F-2)

Adhesive: Acrylic

Backing: Polyester Film

Backing Thickness: One mil (25 micron) / Two mils (50 micron)

Total Thickness:  2.5 mils ( 0,063 mm )  / 3.3 mils( 0,083 mm)

Colors : Yellow, White, Black, Red, Green and Blue.

Temperature Class: 130°C (266°F)

Dielectric Breakdown: 5500 Volts / 7,000 Volts

Insulation Resistance (megohms):>1000000

Breaking Strength: 25 lbs./in (44 N/10mm) / 50 lbs./in (88N/10mm)

Elongation (% at break):  100 /  110

Electrolytic Corrosion Factor: 1.0

Adhesion to Steel: 30 oz/in (3,3N/10mm)

UL 510 Flame Retardant: Yes

Printable: Yes

3M 1350F Tape is available in Yellow, White, Black, Red, Green and Blue.

1350F-1厚 1mil 或 1350F-2 厚 2mil  薄膜，黃, 白或黑紅綠色,  防燃膠黏劑, 抗鬆脫、抗溶劑,用於線圈,變壓器,和電容器的外層封包, 扁平漆包線, 馬達, 可在表面印刷, 66M長

#1350F 與 #1350物理特性同， 唯有#1350F符合WEEE & RoHS環保要求

^{Flame-Retardant Tape 1350T-1 Flame-Retardant, Triple-Layer Polyester Film Tape with Acrylic
Pressure-Sensitive Adhesive}

^{聚酯薄膜膠帶 1350T-1 丙烯酸膠黏劑}

3M 1351T-1 Polyester Film Electrical Tape is made of three layers of 0.5 mil polyester film. Approved for use as reinforced insulation, by standards such as UL 1950, Safety of Information Technology Equipment, including Electrical Business Equipment. Rated for use up to 130°C (266°F), it withstands high temperature conditions. It is designed for use as inner-layer insulation on transformer magnet wire windings where reinforced insulation is specified. Yellow, 1219 mm x 66 m, PE Core, 1 Rls/ctn

Adhesive:  Acrylic Pressure Sensitive
Backing: Triple-Layer PET Film
Backing Thickness: 1.5 mils/0.037 mm
Total Thickness: 3.0 mils /0.08 mm
Color: Yellow
Temperature Class (UL 510): 130°C (266°F)
Adhesion to Steel: 30 oz/in (3.3 N/10mm)
Insulation Resistance: >1000000 megohms
Breaking Strength: 50 lbs./in (88 N/10mm)
Elongation: (% at break) 100
Dielectric Breakdown: 7.0 KV
Electrical Strength per UL 1950-Para 5.1 – Any 2 layer combination: 4.5 KV
UL 510 Flame Retardant: Pass
CTI Rating: Group II
Electrolytic Corrosion Factor: 1.0
厚 1.5 mil PET Film 薄膜，具黃色防燃膠黏劑.三層結構加強絕緣用膠帶, 抗鬆脫、抗溶劑, 抗翹邊﹔用於線圈和電容器的外層封包，展開後光滑平整, 可供自動化設備使用, 可在表面印刷. 66M長

^{1350T-3 Flame Retarded, Triple-Layer Polyester Film Tape with Acrylic Pressure-Sensitive Adhesive}

^{聚酯薄膜膠帶 1350T-3 丙烯酸膠黏劑}

3M 1350T-3 Tape is a flame retarded, triple-layer polyester film tape which has UL component recognition for use as REINFORCED INSULATION as specified in UL 1950 para 2.9.4.2 It also offers excellent solvent resistance, good quick stick, even unwind, and is suitable for use on automatic taping equipment.

3M 1350T -3 Flame Retarded, Triple-layer Polyester Film Tape with Acrylic Pressure-Sensitive Adhesive is designed for use as inner-layer insulation on transformer magnet wire windings where REINFORCED INSULATION is required. 3M Polyester Film Electrical Tape 1350T-3 Yellow, 1219 mm x 66 m, PE Core, 1 Rls/ctn

Adhesive:  Acrylic Pressure Sensitive
Backing: Triple-Layer PET Film
Backing Thickness: 1.5 mils/0.037 mm
Total Thickness: 4.5 mils / 0.11 mm
Color: Yellow
Temperature Class (UL 510): 130°C (266°F)
Adhesion to Steel: 25 oz/in (0.71Kg/in)
Insulation Resistance: >1000000 megohms
Breaking Strength: 77 lbs./in (35 Kg/in)
Elongation: (% at break) 100
Elongation (% at break): 50 %
Dielectric Breakdown: 10.5 KV
Electrical Strength per UL 1950-Para 5.1 – Any 2 layer combination: 5.5 KV
UL 510 Flame Retardant: Pass
CTI: Group II
Electrolytic Corrosion Factor: 1.0

厚 4.5 mil PET film 薄膜，，具黃色防燃膠黏劑.三層結構加強絕緣用膠帶, 抗鬆脫、抗溶劑, 抗翹邊﹔用於線圈和電容器的外層封包，展開後光滑平整, 可供自動化設備使用, 可在表面印刷.60M長

^{3M 1351 Flame-Retardant Tape with Polyester Film Acrylic Pressure-Sensitive Adhesive}

^{聚酯薄膜膠帶 1351F-1 1351F-2  丙烯酸膠黏劑 阻燃膠帶}

3M 1351 Tape is an electrical insulating polyester film tape, which meets the flame-retardancy requirements of UL 510. It consists of materials that are represented in many UL Recognized Insulation Systems and has a UL 130°C temperature rating. It also offers excellent flagging and solvent resistance; good wet grab; smooth, even unwind and is suitable for use on automated equipment.
• UL Recognized Flame Retardant
• UL Recognized Class 130°C
• Excellent Flagging Resistance
• Controlled Release
• Solvent resistant without thermosetting
• Excellent Shelf Life
• UL Recognized CTI Group I

3M 1351 Tape is especially suited for applications such as wrapping coils, capacitors, wire harnesses, transformers, shaded pole motors and fractional horsepower motors.

Properties: 1 mil Film (1351-1) / 2 mil Film (1351-2)

Adhesive: Acrylic

Backing: Polyester Film

Backing Thickness: One mil (25 micron) / Two mils (50 micron)

Total Thickness:  2.5 mils ( 0,063 mm )  / 3.5 mils( 0,088 mm)

Colors : Yellow, White

Temperature Class: 130°C (266°F)

Dielectric Breakdown: 5500 Volts / 7,000 Volts

Insulation Resistance (megohms):  >1000000

Breaking Strength: 25 lbs./in (44 N/10mm) /  50 lbs./in (88N/10mm)

Elongation (% at break):  100 /  110

Electrolytic Corrosion Factor: 1.0

Adhesion to Steel: 30 oz/in (3,3N/10mm)

UL 510 Flame Retardant: Yes

Printable: Yes

1351-1厚 1mil 或 1351-2 厚 2mil  PET Film 薄膜，黃色, 具高導熱係數阻燃膠黏劑, •抗翹邊和抗溶劑, 抗鬆脫,用於線圈,變壓器,和電容器的外層封包, 扁平漆包線, 馬達, 可在表面印刷, 66M長, 展開後光滑平整，可供自動化設備使用.

#1350F 與 #1350其物理特性皆相同，但因應WEEE & RoHS 要求， 唯有#1350F系列可符合此環保要求。

#1351為CTI等級為Group I 之膠帶，而 #1350F為CTI 等級Group II 之膠帶，且 #1351比 #1350F有更好之導熱效果。

#1350F-1與 #1350F-2 代表各為使用1 mil 與 2 mil 厚度之PET 薄膜。

^{Flame-Retardant Tape 1388 Polyester Film Tape with Electrical Insulation Grade
Non-Halogenated Flame Retardant Acrylic Pressure-Sensitive Adhesive}

 ^{3M  1388Y-1 聚酯薄膜膠帶 丙烯酸膠黏劑   無鹵 Non-Halogenated}

3M  1388Y-1 tape is an electrical insulating polyester film tape which meets non-halogenated
requirement and flame retardant requirements according to UL 510 method. It offers smooth unwinding
and is suitable for use on automated equipment.
* Bromide content<900ppm; Total halogen content<1500ppm
* 3M logo printed on backing for identification
* Solvent resistant without thermosetting
* Excellent shelf life
* UL File E305006

Adhesive: electrical grade acrylic
Color: Yellow

Backing: 1 mil polyester film
Total Thickness:  2.0 mils / 0.05 mm
Dielectric Breakdown: 5000 Volts
Insulation Resistance @ 23 C & 96% RH, 96 hrs:  >1000000000000 ohms
Breaking Strength: 25 lbs. / in (44N/10mm)
Elongation (% at break): 100
Adhesion to Steel: 26 oz/in (2.84 N/10mm)
Flame Retardant Pass: UL510 flame test
CTI Group:  II

1388W-1 為白色

^{3M 1618 Polyester Tape Acrylic Pressure-Sensitive Adhesive}

^{3M 1618 聚酯薄膜膠帶 丙烯酸膠黏劑 遮光膠帶}

3M 1618 Tape is an electrical insulating polyester film tape, which meets non-halogen requirement. It offers black adhesive layer, smooth unwinding and proper adhesion level is suitable for use on automated equipment.

* Bromide Content <900ppm: total halogen<1500ppm
* Solvent resistant without thermosetting
* Excellent Shelf Life
* Black adhesive layer coating

* Non-corrosive

* Electrical insulating

Adhesive: Black Color Electrical Grade Acrylic

Backing: Polyester Film

Backing Thickness: One mil (25 micron)

Total Thickness:  2.0 mils ( 0,05 mm )

Colors : Black

Temperature Class: 130°C (266°F)

Dielectric Breakdown: 5000 Volts / 6,500 Volts

Insulation Resistance :  >1000000000000 ohms

Breaking Strength: 25 lbs./in (44 N/10mm)

Elongation (% at break):  100

Adhesion to Steel (Min/normal): 0.75/0.85 kg/in

Adhesion to Steel (Aged/normal): 1 kg/in

1618 厚 1mil 抗溶劑  遮光膠帶 無鹵   內外都是黑色

^{3M 1628 Polyester Tape Acrylic Pressure-Sensitive Adhesive}

^{3M 1628 聚酯薄膜膠帶 丙烯酸膠黏劑 遮光膠帶}

3M 1628 Tape is an electrical insulating polyester film tape, which meets non-halogen requirement. It offers black adhesive layer, smooth unwinding and proper adhesion level is suitable for use on automated equipment.

* Bromide Content <900ppm: total halogen<1500ppm
* Solvent resistant without thermosetting
* Excellent Shelf Life
* Black adhesive layer coating

* Non-corrosive

* Electrical insulating

Adhesive: Black Color Electrical Grade Acrylic

Backing: Polyester Film

Backing Thickness: One mil (25 micron)

Total Thickness:  2.2 mils ( 0.055 mm )

Colors : Black

Temperature Class: 130°C (266°F)

Dielectric Breakdown: 5000 Volts / 7,500 Volts

Insulation Resistance :  >1000000000000 ohms

Breaking Strength: 25 lbs./in (44 N/10mm)

Elongation (% at break):  100

Adhesion to Steel (Min/normal): 0.75/0.85 kg/in

Adhesion to Steel (Aged/normal): 1 kg/in

1628 厚 1mil 抗溶劑  遮光膠帶 無鹵   內外都是黑色

^{3M 1688-1 Polyester Tape Acrylic Pressure-Sensitive Adhesive}

^{3M 1688-1 聚酯薄膜膠帶 丙烯酸膠黏劑 遮光膠帶}

3M 1688-1 tape is an electrical insulating polyester film tape and meets non- halogen requirement. It offers excellent light shielding, proper adhesion level to be suitable for use of automated equipment.

* Bromide Content <900ppm: total halogen<1500ppm
* Solvent resistant without thermosetting
* Excellent Shelf Life
* Black adhesive layer coating

* Non-corrosive

* Electrical insulating

Adhesive: Black Color Electrical Grade Acrylic

Backing: Polyester Film

Backing Thickness: One mil (25 micron)

Total Thickness:  2.4 mils ( 0.06 mm )

Colors : Black

Dielectric Breakdown: 5000 Volts / 7500 Volts

Insulation Resistance :  >1000000000000 ohms

Breaking Strength: 25 lbs./in (44 N/10mm)

Elongation (% at break):  100

Adhesion to Steel (Min/normal): 0.6/0.71kg/in

Adhesion to Steel (Aged/normal): 1.0 kg/in

1688 厚 1mil 抗溶劑  遮光膠帶 無鹵   內外都是黑色

3M Aesthetic Solar Tape 8306

3M  Aesthetic Solar Tape 8306 can be used for many applications where solvent resistant and/or high shear properties are desired. Low outgassing.

UL Component Recognition
8306 is UL listed under UL 510 OANZ2 File
E230409

3M Aesthetic Solar Tape 8306 太陽能模組膠帶 8306膠帶

耐溶劑   高剪切性   太陽能模組修飾暨絕緣膠帶  亦可做為定位膠帶使用  太陽能模組修飾既絕緣用膠帶。

^{3M Polyester Tape 聚酯膠帶 8403 Silicone Adhesive}

^{3M 聚酯膠帶 8403}

3M Polyester Tape 8403 has a silicone adhesive for composite bonding and splicing of many silicone coated papers and films.

• Polyester film that retains flexibility and thermal resistance and is abrasion, chemical and thermal resistant to help reduce failures due to cracking and backing deterioration.
• Silicone adhesive for higher heat resistance than many other adhesives to help reduce failure due to softening, oozing and adhesive transfer.

• Masking edges overlap seams in metal bonding process where the excess epoxy (“flash”) flows onto the tape. Clean-up is complete when the tape is removed. • Protective overall mask on panels to mild caustic or acid bath etching. Helps prevent scratches during handling and provides desired masking during metal bonding and fabrication. • Holding of parts or vacuum bags during bonding process. • Mask for metal in acid or caustic chemical milling baths. • Masking parts in anodizing processes. • Splicing of silicone coated papers and films. • Paint masking of materials subjected to high temperatures.

Backing: Polyester film

Adhesive: Silicone
Color: Translucent green
Lenght:72 yds. (66 m)

Adhesion to Steel: 27 oz./in. width (29 N/100 mm)
Tensile Strength at Break: 46 lbs./in. width (806 N/100 mm)
Elongation at Break: 150%
Backing Thickness: 1.4 mils (0.04 mm)
Total Tape Thickness: 2.4 mils (0.06 mm)
Temperature Use Range: Removes cleanly and remains flexible after 3 hours, 350°F (177°C), in autoclave

#8403 半透明綠色   耐溫到177°C(3小時),  用途是高溫塗裝遮蔽保護 長66M.

^{3M 8901 Polyester Composite Bonding Tape 聚酯膠帶}

^{3M 聚酯膠帶 8901}

3M Composite Bonding Tape 8901 is a high temperature tape with a silicone adhesive for use in composite bagging operations or to help remove flashing after bonding. This tape is designed to provide clean removal during masking operations involving high temperatures and pressure.

• Polyester film that retains flexibility and thermal resistance and is abrasion, chemical and thermal resistant to help reduce failures due to cracking and backing deterioration.
• Silicone adhesive for higher heat resistance than many other adhesives to help reduce failure due to softening, oozing and adhesive transfer.

• Composite and metal bonding as it removes cleanly from stainless steel, anodized aluminum and glass after a 5 hour bake cycle at 350°F (177°C).
• Masking edges of overlap seams in metal bonding process where excess epoxy (“flash”) flows onto tape as clean-up is complete upon tape removal.
• Holding parts or vacuum bags during bonding process.
• Masking parts for powder coat painting.
• Splicing silicone treated materials.
• Composite bagging operations or to remove flashing after bonding.

Adhesive: Silicone
Backing: Polyester
Color: Blue
Lenght:
Adhesion to Steel: 32 oz./in. width (35 N/100 mm)
Tensile Strength at Break: 28 lbs./in. width (490 N/100 mm)
Elongation at Break: 115%
Total Tape Thickness: 2.6 mils (0.06 mm)
Temperature Use Range: Up to 400°F (204°C)

#8902 (藍色)耐溫到204度(1小時), 用途是高溫塗裝遮蔽保護 長66M.

^{3M Polyester Tape 聚酯膠帶 8902 Silicone Adhesive}

^{3M 聚酯膠帶 8902}

3M Polyester Tape 8902 is a high temperature tape with a silicone adhesive for use as a maskant in powder coat painting and is designed to provide clean removal during masking operations involving high temperatures and pressure.

• Polyester film that retains flexibility and thermal resistance and is abrasion, chemical and thermal resistant to help reduce failures due to cracking and backing deterioration.
• Silicone adhesive for higher heat resistance than many other adhesives to help reduce failure due to softening, oozing and adhesive transfer.

• Composite and metal bonding as it removes cleanly from stainless steel, anodized aluminum and glass after a 5 hour bake cycle at 350°F (177°C).
• Masking edges of overlap seams in metal bonding process where excess epoxy (“flash”) flows onto tape as clean-up is complete upon tape removal.
• Holding parts or vacuum bags during bonding process.
• Masking parts for powder coat painting.
• Splicing silicone treated materials.
• Composite bagging operations or to remove flashing after bonding.

Adhesive: Silicone
Color: Blue
Lenght:72 yds. (66 m)
Adhesion to Steel: 40 oz./in. width (44 N/100 mm)
Tensile Strength at Break: 53 lbs./in. width (928 N/100 mm)
Elongation at Break: 130%
Backing Thickness: 2 mils (0.5 mm)
Total Tape Thickness: 3.4 mils (0.09 mm)
Temperature Use Range: Up to 400°F (204°C)

#8902(藍色)耐溫到204度(1小時), 用途是高溫塗裝遮蔽保護 長66M.

^{3M Polyester Tape 850 聚酯薄膜膠帶 丙烯酸膠黏劑 Acrylic Adhesive}

3M Polyester Film Tape 850 can generally be used for splicing and applications where chemical resistance and/or clean removal is necessary. The silver backing is a transparent polyester with a thin layer of aluminum and the gold is a pigmented polyester with a thin layer of aluminum.

Backing: Polyester

Adhesive:  Acrylic / Transparent

Color: Siliver or Black in stock

Lenght: 72 yards

Silver: 42 oz./in. width (46 N/100 mm)
Tensile Strength at Break: 28 lbs./in. width (491 N/100 mm)
Elongation at Break: 120%
Backing Thickness: 0.9 mil (0.02 mm)
Total Tape Thickness: 1.9 mils (0.05 mm)

Water Vapor Transmission Rate - Silver: 0.9 gms. H2O/100 sq. in./24 hrs. (7.75 g/m2/24 hrs.)
Temperature Use Range: -60°F - 300°F (-50°C - 150°C)

• Prolonged exposure to sunlight or hot caustics will cause backing to become brittle and lose tensile strength.
• Thin, high strength polyester film helps reduce failures due to breakage while meeting low caliper requirements.
• Chemical and solvent resistance to help reduce rejects produced from chemical and solvent attack.
• Abrasion resistant to help protect surface from abrasions and rough handling.
 

Application

 銀色 黑色 有貨  不留殘膠 透明, 聚酯薄膜, 抗油, 抗溶劑, 電影底片接合, 記號, 抗磨保護用

^{3M Circuit Plating Tape 851}

^{聚酯薄膜膠帶 851 電鍍遮蔽膠帶}

3M Circuit Plating Tape 851 is a Greenback Printed Circuit Board Tape ( polyester film) with a unique conformable adhesive for printed circuit board masking during electroplating.

• Polyester backing reduces stretch and recovery of tape associated with uneven stop-off line.
• Thick adhesive coating reduces undercutting because adhesive blocks out solutions between fingers.
• Specially designed adhesive that generally performs better when no ovens are used to heat tape and boards.

• For masking printed circuit boards during solder stripping and precious metal plating of fingers.
• Splicing of silicone coated papers.

Adhesive: Blended silicone & rubber
Backing: Polyester Film
Backing Thickness: 0.9 mil (0.02 mm)
Total Thickness: 3.6 mils (0.10 mm)
Color: Transparent green
Tensile Strength at Break: 26.8 lbs./in. width (368 N/100 mm)
Elongation: (% at break) 124%
Adhesion to Steel: 29 oz./in. width (27 N/100 mm)

Temperature Range Max.: 90°C

Standard Roll Length 36yd

3M 851膠帶 半透明綠色 厚 0.9mil 薄膜 具抗化性  用於印刷電路板之鍍金遮蔽

^{3M 851J LED Potting Tape}

^{聚酯薄膜膠帶 851J 電鍍遮蔽膠帶}

3M LED Potting Tape 851J is a green polyester film tape with a unique adhesive system, which effectively seals and protects during the potting process of the manufacturing of LED faceplates.

• Can be applied by hand or automated machine.
• Low shrink polyester film helps to improve optical quality of LED parts.
• Provides the same sealing and protecting properties and produces the same matte finish as 3M  LED Potting Tape 851.
• Unique blended, high cure adhesive for no epoxy leakage and clean removal to improve productivity.
• Reduce optical defects for improved epoxy finish and fewer rejected parts.
• Ultra clean adhesive for reducing contamination and less rework.

• Sealing and protection during LED potting process.

Adhesive: Blended silicone & rubber
Backing: Polyester Film
Backing Thickness: 1.2 mils (0.03 mm)
Total Thickness: 3.6 mils (0.09 mm)
Color: Transparent green
Tensile Strength at Break: 29 lbs./in. width (398 N/100 mm width)
Elongation: (% at break) 250%
Adhesion to Steel: 30 oz./in. width (28 N/100 mm width)

Standard Roll Length 36yd

851J    半透明綠色 厚 1.2 mil 薄膜

^{3M Polyester Tape 853 聚酯薄膜膠帶 丙烯酸膠黏劑 Acrylic Adhesive}

3M Polyester Tape 853 can be used for many applications where solvent resistant and/or high shear properties are desired.   Polyester / Acrylic / Transparent

Adhesion to Steel: 48 oz./in. width (52 N/100 mm)
Tensile Strength at Break: 24 lbs./in. width (421 N/100 mm)
Elongation at Break: 102%
Backing Thickness: 0.9 mil (0.02 mm)
Total Tape Thickness: 2.2 mils (0.05 mm)
Water Vapor Transmission Rate: 1.6 gms H2O/100 sq. in./24 hrs   (24.8 g/m2 24 h)

• High tension splicing applications.
• Quality protective laminate.
• Solvent resistant masking.
• Tape hinge.

 透明, 聚酯薄, 抗油, 抗溶劑 接合 保護用

^{3M Polyester Tapes for High Temperature Applications 綠色耐高溫PET膠帶 8992 8991}

With pressure sensitive silicone adhesive, 3M  Polyester Tapes 8991 and 8992 grab on
contact for reliable masking in most powder coat painting operations with baking at up to
400°F (204°C).
• Sharp, clean paint edge
• 8991 – 1.0 mil polyester backing and 1.4 mil silicone adhesive
• 8992 – 2.0 mil polyester backing and 1.2 mil silicone adhesive
• High dimensional and tensile strength ( 8992 – 37 lbs./in.) for tearing through cured paint
without slivering or breaking
• Resists shrinking, curling, and edge lifting but removes without adhesive residue
• Transparent blue (8991) and transparent dark green (8992) for identification and alignment
• Also used for masking in e-coating, electroplating, and anodizing

3M 綠色耐高溫PET膠帶8992 是一般用途的聚酯材質膠帶，特別適用於高溫油漆遮蔽作業

(例如：漆料塗層)。此款膠帶塗佈矽膠接著劑，可黏合各式難以黏貼的表面，具有化學阻抗性和廣泛的溫度適用範圍。

• 適合高溫作業環境，其溫度範圍從-50ºC (-60ºF)到204ºC (400ºF)
• 在高溫遮蔽作業(例如：粉裝塗層作業)中可乾淨地清除
• 聚酯薄膜具有優良的耐高溫與抗化學品侵蝕性，仍可保持其彈性
• 與3M PET膠帶8891系列相較，此款膠帶的厚度較厚
• 矽膠接著劑可在不同的表面上輕易地清除
• 半透明綠色背層容易辨識和定位

^{3M 9381 Black Polyester Film Tape}

^{3M 9381 聚酯薄膜膠帶 丙烯酸膠黏劑 遮光膠帶}

3M Black polyester tape 9381 is pressure sensitive adhesive tape consisted of black polyester film and acrylic pressure sensitive adhesive, which is designed for light shielding applications.

3M 膠帶 9381   基材 PET   厚度 0.07mm   顏色黑色   抗溶劑  遮光    LCD模组中的遮光