3M 9731 一面矽膠
一面壓克力膠 雙面膠帶
Product Description
3M Double Coated Tapes 9731 and 9731RW have a firm, silicone pressure
sensitive adhesive coated on one side of a polyester film carrier and a high
performance acrylic adhesive coated on the other side of the carrier. The
silicone adhesive features strong holding power to various silicone
surfaces, good temperature performance and good solvent resistance. This
tape also features high adhesion of the acrylic adhesive to a variety of
surfaces along with good high temperature performance and good solvent
resistance.
Product Features
• Silicone adhesive provides good bond to silicone rubber, strong holding
power to various silicone surfaces, good temperature performance and good
solvent resistance.
• 3M Adhesive 350 provides very high adhesion to a wide variety of
materials, excellent shear holding power, high temperature resistance and
excellent UV resistance.
• A thin polyester carrier provides dimensional stability and improved
handling with ease of die cutting and lamination compared to adhesive
transfer tapes.
|
Property |
Values |
|
Notes |
|
Total Tape Thickness without liner |
0.14
mm |
5.5
mil |
|
|
Faceside Adhesive Thickness |
0.041 mm |
1.6
mil |
Faceside
adhesive is on the interior of the roll, exposed when unwound and liner
removed. |
|
Backside Adhesive Thickness |
0.07
mm |
2.9
mil |
Backside
adhesive is on the exterior of the roll, exposed when liner is removed. |
|
Carrier Thickness |
0.025 mm |
1
mil |
|
|
Faceside Adhesive Type |
350
Acrylic Adhesive |
|
Faceside
adhesive is on the interior of the roll, exposed when unwound and liner
removed. |
|
Backside Adhesive Type |
Silicone Adhesive |
|
Backside
adhesive is on the exterior of the roll, exposed when liner is removed. |
|
Adhesive Carrier |
Clear PET (Polyester) |
|
|
|
Primary Liner Type |
58#
Polycoated Kraft |
|
Inner liner
is primary(stays with die-cut part); Outer liner is secondary (removed
first) |
|
Primary Liner Color |
Tan |
|
|
|
Primary Liner Print |
No
Print |
|
|
|
Secondary Liner Type |
Fluoropolymer non-Silicone |
|
Inner liner
is primary(stays with die-cut part); Outer liner is secondary (removed
first) |
|
Secondary Liner Color |
Clear |
|
|
|
Secondary Liner Print |
PET |
|
|
|
Primary Liner Thickness |
0.17
mm |
4.2
mil |
|
|
Secondary Liner Thickness |
0.07
mm |
2.9
mil |
|
Typical Performance
Characteristics
|
350 Acrylic Adhesive Peel
Adhesion |
|
Substrate |
Dwell/Cure Time |
|
4.3 N/cm |
39
oz/in |
ABS |
|
|
4.5 N/cm |
42
oz/in |
Polycarbonate (PC) |
|
|
4.4 N/cm |
40
oz/in |
Polypropylene (PP) |
|
|
4.4 N/cm |
40
oz/in |
Stainless Steel |
15
min @ Room Temperature |
|
4.5 N/cm |
42
oz/in |
Stainless Steel |
72
hr @ Room Temperature |
|
5.2 N/cm |
48
oz/in |
Stainless Steel |
72
hr @ 158°F(70°C) |
Property:
350 Acrylic Adhesive Peel Adhesion
Method: ASTM D3330
|
Silicone Adhesive Peel
Adhesion |
|
Substrate |
Dwell/Cure Time |
|
8.1
N/cm |
74
oz/in |
ABS |
|
|
6.5
N/cm |
60
oz/in |
Polycarbonate (PC) |
|
|
4.8
N/cm |
44
oz/in |
Polypropylene (PP) |
|
|
7.7
N/cm |
71
oz/in |
Stainless Steel |
15
min @ Room Temperature |
|
10.1
N/cm |
93
oz/in |
Stainless Steel |
72
hr @ Room Temperature |
|
13.2
N/cm |
121
oz/in |
Stainless Steel |
72
hr @ 158°F(70°C) |
Property: Silicone Adhesive
Peel Adhesion Method: ASTM
D3330
|
Relative High Temperature
Operating Ranges |
|
Test Condition |
|
177
°C |
350
°F |
Short Term (minutes, hours) |
|
121
°C |
250
°F |
Long
Term (days, weeks) |
Property:
Relative High Temperature Operating Ranges
|
Property |
Values |
Method |
Test Condition |
Notes |
|
Static Shear (faceside) |
6090
min |
ASTM
D3654 |
1000 g @
Room Temperature |
0.5
in² sample size |
|
Static Shear (backside) |
>10,000 min |
ASTM
D3654 |
1000 g @
Room Temperature |
0.5
in² sample size |
|
Static Shear (faceside) |
>10,000 min |
ASTM
D3654 |
500
g @ 70°C (158°F) |
0.5
in² sample size |
|
Static Shear (backside) |
>10,000 min |
ASTM
D3654 |
500
g @ 70°C (158°F) |
0.5
in² sample size |
|
Property |
Values |
Method |
Notes |
Test Condition |
|
Dielectric Strength |
8000 V |
ASTM D1000 |
RMS Voltage/Thickness |
|
|
Volume Resistivity |
3.4 × 10^15 Ω-cm |
ASTM D257 |
|
Room Temperature |
|
350
Acrylic Adhesive Surface Resistivity |
7.4 × 10^15 Ω-cm |
ASTM D257 |
|
Room Temperature |
|
Silicone
Adhesive Surface Resistivity |
2.6 × 10^15 Ω-cm |
ASTM D257 |
|
Room Temperature |
Application
Ideas
•
Applications where bonding
silicone rubber to low surface energy materials is necessary.
|
|
9731 |
|
Total Tape
Thickness without liner (mm) |
0.14 |
|
Faceside
Adhesive Thickness (mm) |
0.041 |
|
Backside
Adhesive Thickness (mm) |
0.07 |
|
Carrier Thickness (mm) |
0.025 |
|
Faceside Adhesive Type |
350
Acrylic Adhesive |
|
Backside Adhesive Type |
Silicone Adhesive |
|
Adhesive Carrier |
Clear PET (Polyester) |
|
Primary Liner Type |
58#
Polycoated Kraft |
|
Primary Liner Color |
Tan |
|
Primary Liner Print |
No
Print |
|
Secondary Liner Type |
Fluoropolymer non-Silicone |
|
Secondary Liner Color |
Clear |
產品介紹
3M 雙面膠帶 9731系列採用高效能的5.5
mil厚基材，內層為矽膠，外層是壓克力膠。
3M 9731-100為0.1mm厚雙面膠帶，一面為矽膠(
透明PET膜)，另一面是壓克力膠(PE塗佈牛皮紙離型紙)。
使用雙面離型, 雙面離型一面為4 mil PET和一面為5 mil
PE塗佈牛皮紙，具耐高溫，中度抗溶劑、適用高至低表面能貼合。
塗佈3M 矽膠和3M 高效能壓克力膠系350號，具良好的高耐溫性 、抗溶劑、初期黏性佳、隨時間增加黏性上升、良好的剪切強度。
* 350 壓克力膠系具優越的抗溶劑特性，可黏合多種材質。包括：低表面能量塑膠、粉末塗料和油性材質
* 矽膠面不需助黏劑即可與矽膠材料有良好的黏著力
* 58號PE塗佈牛皮紙(PCK)離型紙是3m的標準品，良好的吸濕性對模切具有一定的經濟效益
* PET離型膜在高強度模切時可以保護膠面
|