^{3M  8010P 聚醋基材雙面膠帶 Double Coated Acrylic Adhesive PET Tapes}

Faceside adhesive is on the interior of the roll, exposed when unwound.
Backside adhesive is on the exterior of the roll, exposed when liner is removed.

8010 double-coated PET tape features a medium-firm acrylic pressure sensitive adhesive system. The key characteristics of this adhesive include a combination of high performance in adhesion and good shear holding power to a wide variety of materials, including many plastics. 8010 is specially designed for display market applications, such as optically management films attachment, foam, isolative film fixing, and system assembly.

Adhesion to steel: (ASTM D3330, 180 degree peel) (Kg/in)
Backside
20 mins RT 2.5
72 hrs RT 3.1

Relative High Temperature Operating Ranges: Continuously (day-week): 200°F (93°C) /Short Term (minutes-hours): 250°F (121°C)
Relative Solvent Resistance: Good
U. V. Resistance: Good

膠帶使用操作程序
貼合表現與有效貼合面積息息相關, 堅實之感壓程序可明顯增加膠帶之貼合表現. 以下系3M建議之標準膠帶使用操作程序:
(a) 欲達最佳黏著，黏著表面必需清潔與乾燥. 一般建議以布沾取1：1 比例之IPA (Isopropyl Alcohol, 異丙醇) 與水的混合溶液進行表面擦拭清潔後, 待表面完全乾燥. (注意：使用IPA前, 請先參照此溶劑之建議注意事項)。 (b) 在清潔溶劑乾燥後, 將膠帶貼合於黏著表面, 以滾筒或其他方式 (刮板) 平均施以約 15psi (1.05公斤/cm2) 之壓力, 使其有效貼合. (c) 將膠帶離型紙撕除, 然後將欲貼著之材質貼上, 同樣施以15psi 之壓力, 使其有效貼合, 若欲去除氣泡, 建議加大壓力, 以物品所承受之限度為上限. (d) 建議理想的施工溫度介於15℃至38℃之間, 勿低於10℃.(e) 欲使膠帶保存至使用時仍具有穩定的品質, 建議之儲存環境為21℃和50%相對濕度. (f) 黏貼膠帶時，宜以一端先貼合後，再緩壓至另一端，以減低氣泡產生之機率。