^{Flame-Retardant Tape 1350 with Polyester Film and Acrylic Pressure-Sensitive Adhesive}

^{聚酯薄膜膠帶 1350 1350F-1 1350F-2 1350T-1 1350T-3 丙烯酸膠黏劑  PET Tape  RoHS}

3M 1350 Tape is an electrical insulating polyester film tape, which meets the flame-retardancy requirements of UL 510. It consists of materials that are represented in many UL Recognized Insulation Systems and has a UL 130°C temperature rating. It also offers excellent flagging and solvent resistance; good wet grab; smooth, even unwind and is suitable for use on automated equipment. For applications such as wrapping coils, capacitors, wire harnesses, transformers, shaded pole motors and fractional horsepower motors. 2 diffferent size: 1 mil film & 2 mil film backing

Properties: 1 mil Film (1350F-1) / 2 mil Film (1350F-2)

Adhesive: Acrylic

Backing: Polyester Film

Backing Thickness: One mil (25 micron) / Two mils (50 micron)

Total Thickness:  2.5 mils ( 0,063 mm )  / 3.3 mils( 0,083 mm)

Colors : Yellow, White, Black, Red, Green and Blue.

Temperature Class: 130°C (266°F)

Dielectric Breakdown: 5500 Volts / 7,000 Volts

Insulation Resistance (megohms):>1000000

Breaking Strength: 25 lbs./in (44 N/10mm) / 50 lbs./in (88N/10mm)

Elongation (% at break):  100 /  110

Electrolytic Corrosion Factor: 1.0

Adhesion to Steel: 30 oz/in (3,3N/10mm)

UL 510 Flame Retardant: Yes

Printable: Yes

3M 1350F Tape is available in Yellow, White, Black, Red, Green and Blue.

1350F-1厚 1mil 或 1350F-2 厚 2mil  薄膜，黃, 白或黑紅綠色,  防燃膠黏劑, 抗鬆脫、抗溶劑,用於線圈,變壓器,和電容器的外層封包, 扁平漆包線, 馬達, 可在表面印刷, 66M長

#1350F 與 #1350物理特性同， 唯有#1350F符合WEEE & RoHS環保要求。

^{Flame-Retardant Tape 1350T-1 Flame-Retardant, Triple-Layer Polyester Film Tape with Acrylic
Pressure-Sensitive Adhesive}

^{聚酯薄膜膠帶 1350T-1 丙烯酸膠黏劑 PET Tape}

3M 1351T-1 Polyester Film Electrical Tape is made of three layers of 0.5 mil polyester film. Approved for use as reinforced insulation, by standards such as UL 1950, Safety of Information Technology Equipment, including Electrical Business Equipment. Rated for use up to 130°C (266°F), it withstands high temperature conditions. It is designed for use as inner-layer insulation on transformer magnet wire windings where reinforced insulation is specified. Yellow, 1219 mm x 66 m, PE Core, 1 Rls/ctn

Adhesive:  Acrylic Pressure Sensitive
Backing: Triple-Layer PET Film
Backing Thickness: 1.5 mils/0.037 mm
Total Thickness: 3.0 mils /0.08 mm
Color: Yellow
Temperature Class (UL 510): 130°C (266°F)
Adhesion to Steel: 30 oz/in (3.3 N/10mm)
Insulation Resistance: >1000000 megohms
Breaking Strength: 50 lbs./in (88 N/10mm)
Elongation: (% at break) 100
Dielectric Breakdown: 7.0 KV
Electrical Strength per UL 1950-Para 5.1 – Any 2 layer combination: 4.5 KV
UL 510 Flame Retardant: Pass
CTI Rating: Group II
Electrolytic Corrosion Factor: 1.0
厚 1.5 mil 薄膜，具黃色防燃膠黏劑.﹔抗鬆脫、抗溶劑﹔用於線圈和電容器的外層封包，可在表面印刷. 66M長

^{1350T-3 Flame Retarded, Triple-Layer Polyester Film Tape with Acrylic Pressure-Sensitive Adhesive}

^{聚酯薄膜膠帶 1350T-3 丙烯酸膠黏劑 PET Tape}

3M 1350T-3 Tape is a flame retarded, triple-layer polyester film tape which has UL component recognition for use as REINFORCED INSULATION as specified in UL 1950 para 2.9.4.2 It also offers excellent solvent resistance, good quick stick, even unwind, and is suitable for use on automatic taping equipment.

3M 1350T -3 Flame Retarded, Triple-layer Polyester Film Tape with Acrylic Pressure-Sensitive Adhesive is designed for use as inner-layer insulation on transformer magnet wire windings where REINFORCED INSULATION is required. 3M Polyester Film Electrical Tape 1350T-3 Yellow, 1219 mm x 66 m, PE Core, 1 Rls/ctn

Adhesive:  Acrylic Pressure Sensitive
Backing: Triple-Layer PET Film
Backing Thickness: 1.5 mils/0.037 mm
Total Thickness: 4.5 mils / 0.11 mm
Color: Yellow
Temperature Class (UL 510): 130°C (266°F)
Adhesion to Steel: 25 oz/in (0.71Kg/in)
Insulation Resistance: >1000000 megohms
Breaking Strength: 77 lbs./in (35 Kg/in)
Elongation: (% at break) 100
Elongation (% at break): 50 %
Dielectric Breakdown: 10.5 KV
Electrical Strength per UL 1950-Para 5.1 – Any 2 layer combination: 5.5 KV
UL 510 Flame Retardant: Pass
CTI: Group II
Electrolytic Corrosion Factor: 1.0

厚 4.5 mil 薄膜，具黃色防燃膠黏劑.﹔抗鬆脫、抗溶劑﹔用於線圈和電容器的外層封包，可在表面印刷. 長60M

^{Flame-Retardant Tape 1388 Polyester Film Tape with Electrical Insulation Grade
Non-Halogenated Flame Retardant Acrylic Pressure-Sensitive Adhesive}

 ^{3M  1388Y-1 聚酯薄膜膠帶 丙烯酸膠黏劑   PET Tape 無鹵}

3M™ 1388Y-1 tape is an electrical insulating polyester film tape which meets non-halogenated
requirement and flame retardant requirements according to UL 510 method. It offers smooth unwinding
and is suitable for use on automated equipment.
* Bromide content<900ppm; Total halogen content<1500ppm
* 3M logo printed on backing for identification
* Solvent resistant without thermosetting
* Excellent shelf life
* UL File E305006

Adhesive: electrical grade acrylic
Color: Yellow

Backing: 1 mil polyester film
Total Thickness: 2.0 - 2.4 mils / 0.050 - 0.060 mm
Dielectric Breakdown: 5000 Volts
Insulation Resistance @ 23 C & 96% RH, 96 hrs:  >1000000000000 ohms
Breaking Strength: 25 lbs. / in (44N/10mm)
Elongation (% at break): 100
Adhesion to Steel: 26 oz/in (2.84 N/10mm)
Flame Retardant Pass: UL510 flame test
CTI Group:  II

3M? 1388Y-1 Tape is especially suited for applications such as transformers, wrapping coils, shaded pole motors, fractional horsepower motors and various electronic component insulations.