^{3M Electrical Tape 44 Polyester Web-Reinforced Film with Thermosetting Rubber, Pressure-Sensitive Adhesive Non-Halogenated}

^{3M 復合薄膜膠帶 44 聚酯薄膜 ／薄墊   RoHS 無鹵}

3M Electrical Tape 44 is a combination polyester film/polyester web coated with a rubber thermosetting pressure-sensitive adhesive. For maximum solvent resistance and holding properties, the tape should be thermoset at one of the following cycles:
1 hour @ 150°C (300°F)
2 hours @ 135°C (275°F)
3 hours @ 120°C (250°F)
The tape is suggested for use in stick-wound coils/transformers and in bobbin-wound coils for banding, anchoring, and insulating, and for protecting start wires, leads, terminal strips, insulation paper, end turns and connections in motors and transformers.

Thickness: 5.5 mils (0.139 mm)
Breaking Strength: 40 lbs./in (70 N/10 mm)
Elongation: 50%
Adhesion to Steel: 65 oz/in (7.1 N/10 mm)
Puncture Resistance: 12 lbs. (5.4 kg)
Dielectric Strength: 5500V
Temperature Class: 130°C
Insulation Resistance: >1x106 megohms
Electrolytic Corrosion Factor: 1.0

Halogen Content: Chlorine <0.09%      Bromine <0.004%  低鹵產品

歐盟對於無鉛及無鹵的標準皆以小於 某特定之ppm為規範

檔牆膠帶 無鹵素膠帶 抗穿次、電氣性能極佳、堅韌、從形性高﹔用於絕緣、固定和捆紮 馬達和變壓 長90M

^{3M Electrical Tape 44A Polyester Web-Reinforced Film with Acrylic Adhesive Non-Halogenated}

^{3M 復合薄膜膠帶 44A 聚酯薄膜 丙烯酸膠黏劑 無鹵}

Thickness: 5.5 mils (0.139 mm)
Breaking Strength: 40 lbs./in (70 N/10 mm)
Elongation: 50%
Adhesion to Steel: 20 oz/in
Puncture Resistance: 12 lbs. (5.4 kg)
Dielectric Strength: 5500V
Temperature Class: 130°C
Insulation Resistance: >1x106 megohms
Electrolytic Corrosion Factor: 1.0

^{3M Electrical Tape 44HT Polyester Web-Reinforced Film with High-Tack Thermosetting Rubber Pressure-Sensitive Adhesive}

3M Electrical Tape 44HT is a combination polyester film/polyester web coated with a rubber thermosetting pressure-sensitive adhesive. The tape is a high-tack, puncture resistant, conformable tape with excellent electrical properties.

Color: Caramel Translucent

Adhesive: Rubber Thermosetting

Backing Thickness: 5.0 mils (0,127 mm)

Breaking Strength: 40 lbs/in (70 N/10 mm)

Elongation (% at break): 50%

Puncture Resistance (per Federal Spec L-T-001512) : 12 lbs (5.4 kg)

Adhesion to Steel 35 oz/in (3.8 N/10 mm)

Dielectric Breakdown: 5500 V

Insulation Resistance > 1 x 1000000 megohms

CTI Material: Group 1

Electrolytic Corrosion Factor (per 3M Test Method): 1.0

其他復合薄膜膠帶 Others 44D-A  44T-A

^{3M 55 Tape Polyester Film/Mat Composite with Rubber Thermosetting Pressure-Sensitive Adhesive}

^{3M 合金復合薄膜膠帶 55 聚酯薄膜 ／薄墊}

3M 55 Tape has excellent physical and electrical characteristics. This tape is especially well suited for use as a coil cover. For end turns, lead pad and core layer and crossover insulation.

*Thickness:  7.5 mils (.190 mm)

*Tensile Strength: 35 lbs. (62 N/10 mm)

Adhesion to Steel: 80 oz/in (8,7 N/10 mm)

Unwind at 90 in/min: 12 oz/in (1,3 N/10 mm)

*Elongation: 30%

Adhesion to Backing: 20 oz.in (2,9 N/10 mm)

*Dielectric strength: 6000 V

*Insulation Resistance: > 1 x 106

**Electrolytic Corrosion Factor: 1.0 Ratio

抗撕裂、抗刺穿、抗磨性﹔用於線圈封包、引線襯墊和線芯、外層及線間絕緣。

^{3M Composite Film Tape MR94 MR94B Polyester Film/Non-Woven Laminate Tape with Rubber, Thermosetting, Pressure-Sensitive Adhesive}

^{3M 復合薄膜膠帶 MR94 MR94B 聚酯薄膜 ／薄墊   已停產 No Longer Available}

· Excellent electrical properties / · Conformable / · Puncture resistant / · UL Recognized Class 130°C / · Available in tan (MR 94) 棕色 and black (MR 94B)黑色

3M Composite Film Electrical Tape MR94 is best used for insulating, anchoring, banding and protecting start lead wires, terminal strips, end turns and connections on motors and transformers. This product is especially suited for applications such as stick-wound coils/transformers and bobbin-wound coils; for banding, anchoring and insulating; and for protecting
start wires, leads, terminal strips, insulation paper, end turns and connections in motors and transformers. To achieve maximum solvent resistance and holding performance, we suggest thermosetting the tape at one of the following cycles:
1 hour @ 150°C (300° F) / 2 hours @ 135°C (275° F) / 3 hours @ 120°C (250° F)

Color:  Tan or Black
Thickness: 4.0 mils (0.101mm) 總厚
Breaking Strength at Break:  30 lb./in (53 N/10 mm)
Elongation at Break: 50%
Adhesion to Steel: 40 oz/in (4.4 N/10 mm)
Dielectric Breakdown: 5000V
Temperature Class: 130°C
Insulation Resistance: >1x106 megohms
Electrolytic Corrosion Factor: 1.0 ratio

電氣性能極佳、從形性高，用於絕緣、固定、捆紮及保護起始引線、末端帶、 末端折回及馬達和變壓器的連接。

^{3M ETA-S80 Polyester Aluminum Polyester Composite Film}

^{3M ETA-S80 聚酯薄膜鋁箔復合膠帶      No Stock}

ETA-S80

Backing: Polyester/aluminum/polyester composite film

Adhesive: Clear Acrylic PSA (0.025mm) with release paper

Application: EMI shielding, Electrical insulating & holding application, Anti-curling.

Total Thickness ( w/o release liner): 0.078mm

Tensile strength at break: 54 N/cm

Elongation at break: 75%

Adhesion (180 degree peel): 6.5 /N/cm

3M ETA-S80 抗捲曲膠帶, PAP Tape, Polyester + Aluminum + Polyester 膠帶

3M ETA-S80 是透明PET+鋁+透明PET,  長時間持續溫度可達85C.

PET貼合之鋁箔,具抗氧化,溶劑,油料,EMI防護及ESD等特性.

^{3M ETA-S60B Polyester Aluminum Polyester Composite Film  ETA-S60BB}

^{3M ETA-S60B ETA-S60BB 聚酯薄膜鋁箔復合膠帶}

ETA-S60B  ETA-S60BB

3M ETA-S60B 是黑色PET+鋁+黑色PET+透明非導電膠.

3M ETA-S60BB 是黑色PET+鋁+黑色PET+黑色非導電膠.

Backing: Polyester/aluminum/polyester composite film

Adhesive: Acrylic PSA (0.02mm) with release paper 

Application: EMI shielding, Light Shielding, Electrical insulating & holding application, Anti-curling.

Total Thickness ( w/o release liner): 0.061mm

Tensile strength at break: 44 N/cm

Elongation at break: 66%

Adhesion (180 degree peel): 4.6 /N/cm

3M ETA-S60B  ETA-S60BB 抗捲曲膠帶,  長時間持續溫度可達85C

PET貼合之鋁箔,具抗氧化,溶劑,油料,EMI防護及ESD等特性.

ETA-C65 = 透明PET+鋁+導電膠

ETA-C65B = 黑色PET+鋁+導電膠

Total Thickness ( w/o release liner): 0.065mm

Tensile strength at break: 44 N/cm

Elongation at break: 66%

Adhesion (180 degree peel): 3.0 /N/cm

ETA-N65 = 透明PET+鋁+非導電膠

Total Thickness ( w/o release liner): 0.065mm

Tensile strength at break: 44 N/cm

Elongation at break: 66%

Adhesion (180 degree peel): 3.0 /N/cm